Scientists with the U.S. Department of Energy’s Lawrence Berkeley National Laboratory (Berkeley Lab) have mimicked the structure of mother of pearl to create what may well be the toughest ceramic ever produced.
Through the controlled freezing of suspensions in water of an aluminum oxide (alumina) and the addition of a well known polymer, polymethylmethacrylate (PMMA), a team of researchers has produced ceramics that are 300 times tougher than their constituent components. The team was led by Robert Ritchie, who holds joint appointments with Berkeley Lab’s Materials Sciences Division and the Materials Science and Engineering Department at the University of California, Berkeley.
“We have emulated nature’s toughening mechanisms to make ice-templated alumina hybrids that are comparable in specific strength and toughness to aluminum alloys,” says Ritchie. “We believe these model materials can be used to identify key microstructural features that should guide the future synthesis of bio-inspired, yet non-biological, light-weight structural materials with unique strength and toughness.”
The results of this research were reported in the December 5, 2008 issue of the journal Science, in a paper entitled:“Tough, bio-inspired hybrid materials.” Co-authoring the paper with Ritchie were Etienne Munch, Max Launey, Daan Hein Alsem, Eduardo Saiz and Antoni Tomsia.
Mother of pearl, or nacre, the inner lining of the shells of abalone, mussels and certain other mollusks, is renowned for both its iridescent beauty and its amazing toughness. Nacre is 95-percent aragonite, a hard but brittle calcium carbonate mineral, with the rest of it made up of soft organic molecules. Yet nacre can be 3,000 times (in energy terms) more resistant to fracture than aragonite. No human-synthesized composite outperforms its constituent materials by such a wide margin. The problem has been that nacre’s remarkable strength is derived from a structural architecture that varies over lengths of scale ranging from nanometers to micrometers. Human engineering has not been able to replicate these length scale variances.
Two years ago, however, Berkeley Lab researchers Tomsia and Saiz found a way to improve the strength of bone substitutes through a processing technique that involved the freezing of seawater. This process yielded a ceramic that was four times stronger than artificial bone. When seawater freezes, ice crystals form a scaffolding of thin layers. These layers are pure ice because during their formation impurities, such as salt and microorganisms, are expelled and entrapped in the space between the layers. The resulting architecture roughly resembles that of nacre.
“Since seawater can freeze like a layered material, we allowed nature to guide the process by which we were able to freeze-cast ceramics that mimicked nacre,” said Tomsia when this research was reported.
In this latest research, Ritchie, working with Tomsia and Saiz, refined the freeze-casting technique and applied it to alumina/PMMA hybrid materials to create large porous ceramic scaffolds that much more closely mirrored the complex hierarchical microstructure of nacre. To do this, they first employed directional freezing to promote the formation of thin layers (lamellae) of ice that served as templates for the creation of the layered alumina scaffolds. After the ice was removed, spaces between the alumina lamellae were filled with polymer.
“The key to material toughness is the ability to dissipate strain energy,” says Ritchie. “Infiltrating the spaces between the alumina layers with polymer allows the hard alumina layers to slide (by a small amount) over one another when load is applied, thereby dissipating strain energy. The polymer acts as a lubricant, like the oil in an automobile engine.”
In addition to making the lamellar scaffolds, the team was also able to fabricate nacre-like “brick-and-mortar” structures with very high alumina content. They did this by collapsing the scaffolds in a perpendicular direction to the layers then sintering the resulting alumina “bricks” to promote brick densification and the formation of ceramic bridges between individual bricks.
Says Saiz, “Using such techniques, we have made complex hierarchical architectures where we can refine the lamellae thickness, control their macroscopic orientation, manipulate the chemistry and roughness of the inter-lamellae interfaces, and generate a given density of inorganic bridges, all over a range of size-scales.”